ChiMei WONDERLITE® PC-110 PC is a high-performance polycarbonate engineering plastic featuring exceptional optical transparency, mechanical strength, and thermal stability, making it ideal for precision injection molding.
| Manufacturer | Chimei |
|---|---|
| Density | 1.20 g/cm³ |
| MVR | 10 cm³/10 min |
| Tensile Strength at Yield | 65.0 MPa |
| Elongation at Break | 120 % |
Note: See the product description for additional technical specifications
ChiMei WONDERLITE® PC-110 PC is a high-performance polycarbonate engineering plastic carefully developed by ChiMei Corporation. As a global leader in polymer material supply, ChiMei enjoys an exceptional industry reputation in the field of thermoplastics. This product appears in the form of high-transparency pelletized solids, featuring outstanding optical properties and mechanical strength, making it an ideal choice for high-end manufacturing and precision injection molding.
In modern industrial manufacturing, WONDERLITE® PC-110 PC is widely applied in electronic and electrical components, automotive parts, office equipment housings, and various high-quality consumer goods due to its well-balanced performance.
| Physical Properties | Test Value | Test Unit | Test Standard |
| Density 23 °C | 1.2 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MFR) 300 °C, 1.2 kg | 10 | cm³/10 min | ISO 1133 |
| Mold Shrinkage | 0.50-0.70 | % | ISO 294-4 |
| Mechanical Properties | Test Value | Test Unit | Test Standard |
| Tensile Stress, Yield 50 mm/min | 65 | MPa | ISO 527-2/50 |
| Tensile Stress, Break 50 mm/min | 75 | MPa | ISO 527-2/50 |
| Tensile Strain, Break 50 mm/min | 120 | % | ISO 527-2/50 |
| Flexural Modulus 2 mm/min | 2400 | MPa | ISO 178 |
| Flexural Strength 2 mm/min | 90 | MPa | ISO 178 |
| Charpy Impact Strength, Notched 23 °C | 75 | kJ/m² | ISO 179 |
| Izod Impact Strength, Notched 23 °C | 75 | kJ/m² | ISO 180/1A |
| Thermal Properties | Test Value | Test Unit | Test Standard |
| Deflection Temperature Under Load, Unannealed (0.45 MPa) | 143 | °C | ISO 75-2/B |
| Deflection Temperature Under Load, 1.8 MPa Annealed | 128 | °C | ISO 75-2/A |
| Vicat Softening Temperature 50 °C/h, 1 kg | 150 | °C | ISO 306/A50 |
| Vicat Softening Temperature 50 °C/h, 5 kg | 145 | °C | ISO 306/B50 |
| Coefficient of Linear Thermal Expansion (CTE), Flow | 6.0E-5-8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability Rating 2.5 mm | V-2 | — | UL 94 |
The technical data sheet (TDS) of ChiMei WONDERLITE® PC-110 PC material from ChiMei corporation, if there are differences, please refer to the official website of ChiMei corporation.
Exceptional Impact Strength: Features extremely high Charpy and Izod notched impact strength (75 kJ/m²), performing exceptionally well when enduring accidental drops or high-intensity mechanical stress.
Outstanding Optical Transparency and Appearance: The amorphous structure grants it high light transmittance and a clean surface, capable of meeting the stringent aesthetic requirements of high-end consumer electronics and optical housings.
Excellent Dimensional Stability: Maintains extremely low linear expansion coefficients and stable mold shrinkage across a broad temperature range, ensuring dimensional tolerances for precision-molded parts.
Good Heat Resistance: Performance in heat deflection temperature and Vicat softening point is outstanding, allowing adaptation to long-term stable operation in high-temperature working environments.
Stable Processing Performance: Melt flow index performance is well-balanced, matching standard injection molding processes, helping to shorten production cycles and reduce defective rates.
Consumer Electronics: Extensively used to manufacture laptop housings, mobile phone components, charger casings, and various high-grade transparent digital accessories.
Appliance Housings and Components: Suitable for hairdryer shells, switch and socket panels, small kitchen appliance structural parts, and other scenarios requiring a balance of insulation properties and aesthetics.
Automotive Components: Frequently utilized for automotive interior parts, light assemblies, sensor housings, and transparent instrument cluster protective covers.
Safety Protection and Medical Devices: Can be used to manufacture protective face shields, transparent observation windows for medical equipment, and small instrument housings.
Toys and Daily Goods: High impact resistance and environmental characteristics make it suitable for manufacturing high-quality children’s toys and durable transparent containers.
Q1: What kind of drying treatment is required for ChiMei WONDERLITE® PC-110 PC before injection molding?
A: Because polycarbonate (PC) possesses trace hygroscopicity, failing to perform adequate drying prior to high-temperature processing will result in material degradation and produce silver streaks or bubbles. It is recommended to use a hot-air circulation dryer before injection molding, drying at 120 °C for 3 to 4 hours to control moisture content below 0.02%.
Q2: Compared to PMMA (Acrylic), what performance advantages does PC-110 offer?
A: Although PMMA features extremely high surface hardness and light transmittance, its impact resistance tends to be brittle. In contrast, ChiMei WONDERLITE® PC-110 PC belongs to high-impact engineering plastics, possessing unmatched toughness and impact strength (notched impact strength reaching 75 kJ/m²), making it much more suitable for structural parts and housings requiring resistance to mechanical stress, drop protection, or shock resistance.
Q3: Does this grade comply with relevant environmental and safety compliance standards?
A: Yes. ChiMei WONDERLITE® PC-110 PC complies with international environmental standards (such as RoHS and REACH directives), and achieves a UL 94 V-2 level in flammability performance, capable of meeting compliance requirements for mainstream global electronic, electrical, and industrial manufacturing markets.
Submit your inquiry today and receive a professional competitive price tailored to your project requirements.